    Default Tig Welding Chromoly Question Taking A Second Pass?

    Hi everyone. I have been doing a lot of practice tig welding with .040 er70-2 filler rod and .035 wall 4130 tubing from Aircraft Spruce. It has been a long steep road but I am finally getting a handle on it. I have been using pulse settings (80A peak, 15 base, 2 pulses per second) with the lay wire technique. My torch is a CK130 with 1/16" 2% lanthenated tungsten. My welds are looking better on the first pass. I can make them look better if I take a second pass adding filler rod in the thin spots. I am still practicing and my goal is to get it on the first pass but I was wondering if it is a bad practice to go over the welds twice?

    Fernando Carcao

  2. #2
    Join Date
    Mar 2009
    Location
    Tulsa, Oklahoma, United States
    Posts
    2,983
    Post Thanks / Like
    Mentioned
    0 Post(s)
    Tagged
    0 Thread(s)

    Default Re: Tig Welding Chromoly Question Taking A Second Pass?

    A lot of builders will run a fusion pass and a filler pass on titanium. On anything else, it's best to weld it once and be done with it.
    Like you said, work on getting it right on the first pass.
    Eric Doswell, aka Edoz
    Summoner of Crickets
    http://edozbicycles.wordpress.com/
    http://www.flickr.com/photos/edozbicycles/
    In Before the Lock

  3. #3
    Join Date
    Mar 2019
    Posts
    22
    Post Thanks / Like
    Mentioned
    0 Post(s)
    Tagged
    0 Thread(s)

    Default Re: Tig Welding Chromoly Question Taking A Second Pass?

    I’m getting there. I have been trying to develop a sequence in order to be more consistent. I can make it look much prettier if I go over it twice. I can see how going over it twice can be a poor practice.
    I’ll keep practicing:
    161253E5-30DA-4AE8-81C6-B2B59B45373B.jpg
    49127D0F-661C-49AC-81B0-9A26175094DE.jpg
    E32D4CD7-CF20-4FD5-8500-BAB6E6E1AFA1.jpg

  4. #4
    Join Date
    Jun 2008
    Location
    Portland
    Posts
    1,759
    Post Thanks / Like
    Mentioned
    4 Post(s)
    Tagged
    0 Thread(s)

    Default Re: Tig Welding Chromoly Question Taking A Second Pass?

    Nice work in committing to practice.

    How high is your amperage set? One of the things I noticed when I was an instructor at UBI is that most beginners are afraid of using too much heat and avoid it by going slow and using lower amps. A large portion of your beads are dull and grey, that's a sign of too much heat input. It might seem counterintuitive, but if you set your machine up to 150A, go deeper into the pedal and move faster, you'll input less heat into the joint and get better flowout of the filler. You'll probably blow open a few holes, but filling holes is part of the journey and you might as well become an expert at that before you start welding frames. Be sure to practice some 60° joints too

    The next time you're picking up weld rod for practice, get a little ER70S-6 and give it a shot. I've always felt that S-2 felt really grainy when trying to push a lot of rod into a puddle (like in an acute part of a joint). The S-6 seems to flow out a little better without having to push on it as hard. Don from Anvil turned a lot of builders on to Weldmold 880T, which flows out very nicely but costs a bit more than the ER70 rod.
    Sean Chaney
    www.vertigocycles.com
    a peek behind the curtain

  5. #5
    Join Date
    Mar 2019
    Posts
    22
    Post Thanks / Like
    Mentioned
    0 Post(s)
    Tagged
    0 Thread(s)

    Default Re: Tig Welding Chromoly Question Taking A Second Pass?

    Quote Originally Posted by VertigoCycles View Post
    Nice work in committing to practice.
    We
    How high is your amperage set? One of the things I noticed when I was an instructor at UBI is that most beginners are afraid of using too much heat and avoid it by going slow and using lower amps. A large portion of your beads are dull and grey, that's a sign of too much heat input. It might seem counterintuitive, but if you set your machine up to 150A, go deeper into the pedal and move faster, you'll input less heat into the joint and get better flowout of the filler. You'll probably blow open a few holes, but filling holes is part of the journey and you might as well become an expert at that before you start welding frames. Be sure to practice some 60° joints too

    The next time you're picking up weld rod for practice, get a little ER70S-6 and give it a shot. I've always felt that S-2 felt really grainy when trying to push a lot of rod into a puddle (like in an acute part of a joint). The S-6 seems to flow out a little better without having to push on it as hard. Don from Anvil turned a lot of builders on to Weldmold 880T, which flows out very nicely but costs a bit more than the ER70 rod.
    I’m using 80-85 amps. Most of the joints look cooked because of the multiple passes I took. I am getting better on the first pass but need more practice. I was using weldmold 880 to practice at the beginning but decided to switch to ER70S-2 because it is readily available here in Canada. I am saving the weldmold 880 for use on actual frames. I’ll pick up some ER70S-6 and give it a try. I am going to make some 60 degree practice welds, thanks for pointing that out. I have been making 90 degree welds this whole time.

  6. #6
    Join Date
    Mar 2019
    Posts
    22
    Post Thanks / Like
    Mentioned
    0 Post(s)
    Tagged
    0 Thread(s)

    Default Re: Tig Welding Chromoly Question Taking A Second Pass?

    Welding 60 degree mitering is so much harder than 90! Thanks for raising the bar! I would much rather have taken a lesson from a pro but not possible with all the lock downs. I’ll keep self isolating with my family and my torch.

    EC05A6BE-046B-4EB3-9170-81321BA59FCE.jpg

  7. #7
    Join Date
    Mar 2019
    Posts
    22
    Post Thanks / Like
    Mentioned
    0 Post(s)
    Tagged
    0 Thread(s)

    Default Re: Tig Welding Chromoly Question Taking A Second Pass?


  8. #8
    Join Date
    Mar 2019
    Posts
    22
    Post Thanks / Like
    Mentioned
    0 Post(s)
    Tagged
    0 Thread(s)

    Default Re: Tig Welding Chromoly Question Taking A Second Pass?

    I switched from er70s-2 to 880 filler rod and noticed the difference immediately. Looking forward to trying the er70s-6. I really appreciate the feedback.

    3378662C-6474-4C8B-A814-7E1C4423023B.jpg

  9. #9
    Join Date
    Mar 2019
    Posts
    22
    Post Thanks / Like
    Mentioned
    0 Post(s)
    Tagged
    0 Thread(s)

    Default Re: Tig Welding Chromoly Question Taking A Second Pass?

    B7F29342-CA1E-4C6D-B556-4A49B023F452.jpg

    More practice on .035 to .035 material. I find it easier to weld tubes of the same thickness. When welding .035 to .080 (like seat tube to bottom bracket) I have to be very careful with my torch angle so as to not burn holes through the thinner material. Below is 36x 1.5” .080 tube with .035 tubes welded on four sides.

    B8F38346-26E6-48CA-819F-0B8963A6E730.jpg

  10. #10
    Join Date
    Mar 2019
    Posts
    22
    Post Thanks / Like
    Mentioned
    0 Post(s)
    Tagged
    0 Thread(s)

  11. #11
    Join Date
    Mar 2019
    Posts
    22
    Post Thanks / Like
    Mentioned
    0 Post(s)
    Tagged
    0 Thread(s)

    Default Re: Tig Welding Chromoly Question Taking A Second Pass?

    Starting to feel more confident.
    C2B247F9-C688-4C40-AC9E-194BF1B1FD24.jpg

  12. #12
    Join Date
    Mar 2019
    Posts
    22
    Post Thanks / Like
    Mentioned
    0 Post(s)
    Tagged
    0 Thread(s)

  13. #13
    Join Date
    Mar 2019
    Posts
    22
    Post Thanks / Like
    Mentioned
    0 Post(s)
    Tagged
    0 Thread(s)

    Default Re: Tig Welding Chromoly Question Taking A Second Pass?


  14. #14
    Join Date
    Mar 2019
    Posts
    22
    Post Thanks / Like
    Mentioned
    0 Post(s)
    Tagged
    0 Thread(s)

    Default Re: Tig Welding Chromoly Question Taking A Second Pass?

    Still practicing almost daily. Finally started on a bike.

    A2DDAB9C-0FE0-4CB7-88CF-4A273D936E90.jpeg
    E52AFCB0-582F-4DBA-8D60-E2C9A0D27700.jpg
    3637DE23-E2AA-4DD4-B79D-2899422EF6B5.jpg

    Thanks to all the pros here that are always willing to help!

    Fernando

  15. #15
    Join Date
    May 2016
    Posts
    174
    Post Thanks / Like
    Mentioned
    0 Post(s)
    Tagged
    0 Thread(s)

    Default Re: Tig Welding Chromoly Question Taking A Second Pass?

    Looking good Fernando!

Similar Threads

  1. Titanium welding question
    By ZackR in forum The Frame Forum@VSalon
    Replies: 9
    Last Post: 08-26-2016, 07:29 PM
  2. Question about welding
    By Plan_B in forum The Frame Forum@VSalon
    Replies: 8
    Last Post: 06-12-2016, 05:08 PM
  3. Newb Welding Question: Pitting
    By roburrito in forum The Frame Forum@VSalon
    Replies: 5
    Last Post: 07-04-2012, 01:20 PM

Bookmarks

Bookmarks

Posting Permissions

  • You may not post new threads
  • You may not post replies
  • You may not post attachments
  • You may not edit your posts
  •